Structures by: Glaser F. W.

Total: 13

(Cr Mo B4)0.5

B2Cr0.5Mo0.5

Post, B.Moskowitz, D.Glaser, F.W.

Acta Metallurgica (1954) 2, 20-25

a=3.01Å   b=3.01Å   c=3.12Å

α=90°   β=90°   γ=120°

(Cr0.5 Ta0.5) B2

B2Cr0.5Ta0.5

Post, B.Glaser, F.W.Moskowitz, D.

Acta Metallurgica (1954) 2, 20-25

a=3.025Å   b=3.025Å   c=3.21Å

α=90°   β=90°   γ=120°

(Cr0.5 Ti0.5) B2

B2Cr0.5Ti0.5

Glaser, F.W.Post, B.Moskowitz, D.

Acta Metallurgica (1954) 2, 20-25

a=2.99Å   b=2.99Å   c=3.14Å

α=90°   β=90°   γ=120°

(Cr0.5 V0.5) B2

B2Cr0.5V0.5

Moskowitz, D.Glaser, F.W.Post, B.

Acta Metallurgica (1954) 2, 20-25

a=2.99Å   b=2.99Å   c=3.045Å

α=90°   β=90°   γ=120°

Cr B2

B2Cr

Moskowitz, D.Glaser, F.W.Post, B.

Acta Metallurgica (1954) 2, 20-25

a=2.97Å   b=2.97Å   c=3.07Å

α=90°   β=90°   γ=120°

(Hf0.5 Ti0.5) B2

B2Hf0.5Ti0.5

Moskowitz, D.Glaser, F.W.Post, B.

Acta Metallurgica (1954) 2, 20-25

a=3.085Å   b=3.085Å   c=3.368Å

α=90°   β=90°   γ=120°

(Mo Ti B4)0.5

B2Mo0.5Ti0.5

Glaser, F.W.Post, B.Moskowitz, D.

Acta Metallurgica (1954) 2, 20-25

a=3.035Å   b=3.035Å   c=3.206Å

α=90°   β=90°   γ=120°

(Mo Zr B4)0.5

B2Mo0.5Zr0.5

Post, B.Glaser, F.W.Moskowitz, D.

Acta Metallurgica (1954) 2, 20-25

a=3.085Å   b=3.085Å   c=3.4Å

α=90°   β=90°   γ=120°

(Nb Ti B4)0.5

B2Nb0.5Ti0.5

Glaser, F.W.Moskowitz, D.Post, B.

Acta Metallurgica (1954) 2, 20-25

a=3.06Å   b=3.06Å   c=3.264Å

α=90°   β=90°   γ=120°

(Nb Zr B4)0.5

B2Nb0.5Zr0.5

Post, B.Moskowitz, D.Glaser, F.W.

Acta Metallurgica (1954) 2, 20-25

a=3.128Å   b=3.128Å   c=3.42Å

α=90°   β=90°   γ=120°

(Ta0.5 Ti0.5) B2

B2Ta0.5Ti0.5

Moskowitz, D.Glaser, F.W.Post, B.

Acta Metallurgica (1954) 2, 20-25

a=3.05Å   b=3.05Å   c=3.246Å

α=90°   β=90°   γ=120°

(Ta0.5 Zr0.5) B2

B2Ta0.5Zr0.5

Post, B.Glaser, F.W.Moskowitz, D.

Acta Metallurgica (1954) 2, 20-25

a=3.12Å   b=3.12Å   c=3.4Å

α=90°   β=90°   γ=120°

(Ti0.5 Zr0.5) B2

B2Ti0.5Zr0.5

Glaser, F.W.Post, B.Moskowitz, D.

Acta Metallurgica (1954) 2, 20-25

a=3.098Å   b=3.098Å   c=3.39Å

α=90°   β=90°   γ=120°